Author Huang, Adolf Chun-Chiung, 1941-

Title Precipitation hardening of a Mg - 3.5 wt. % Th - 1. wt. % Mn alloy / by Adolf Chun-Chiung Huang.

Published 1969.
LOCATION CALL # STATUS
 MST DEPOSITORY  THESIS T 2267 c.2  NOT CHECKED OUT
 MST DEPOSITORY  THESIS T 2262/2279,2287/2288  MICROFILM    NOT CHECKED OUT
 MST DEPOSITORY  THESIS T 2267    NOT CHECKED OUT
Description vii, 36 leaves : illustrations ; 28 cm.
Summary "The precipitation process in a Mg - 3.5 wt. % Th - 1. wt. % Mn alloy during aging at 260°, 350° and 400°C was determined principally by transmission electron microscopy. At 350° and 400°C, general precipitation of the equilibrium Mg₄Th phase moderately hardens the alloy. No transition lattice of this phase was seen. The Mg₄Th precipitate forms initially as disc shaped plates parallel either to the prism or basal plane of the matrix...During prolonged aging at 400°C the plates lengthen into long laths on either of the above planes in the close packed direction...At 260°C an unidentified G. P. zone appearing precipitate forms"--Abstract, leaf ii.
Notes Vita.
Includes bibliographical references (leaf 33).
M.S. University of Missouri--Rolla 1969.
Subjects Precipitation hardening.
Magnesium alloys -- Experiments.
Microhardness -- Experiments.
Other Titles MST Thesis. Metallurgical Engineering (M.S., 1969)
OCLC/WorldCat Number 6009439
Author Huang, Adolf Chun-Chiung, 1941-
Title Precipitation hardening of a Mg - 3.5 wt. % Th - 1. wt. % Mn alloy / by Adolf Chun-Chiung Huang.
Subjects Precipitation hardening.
Magnesium alloys -- Experiments.
Microhardness -- Experiments.